US10910654(JAPAN SCIENCE & TECH AGENCY [JP])
Example 1-1: Production of Fuel Cell Including, in Anode, Fuel Cell Electrode Catalyst of the Present Invention
【０１０６】
  ＜実施例１－１：本発明に係る燃料電池用電極触媒をアノードに含有する燃料電池セルの製造＞

A membrane electrode assembly (MEA) was produced by

(i) providing, on the hydrogen electrode (anode) side, a carbon cloth to which the molecular metal complex was applied and (ii) providing, on the oxygen electrode (cathode) side, a carbon cloth to which platinum carbon TEC10V50E (manufactured by Takana Kikinzoku Kogyo K.K.) was applied so that a polymer membrane (Nafion (Registered Trademark) NRE212, manufactured by DuPont) was sandwiched by these carbon cloths.
高分子膜（ナフィオン（登録商標）NRE212、デュポン社製）を、水素極（アノード）側を分子性金属錯体が塗工されたカーボンクロスで、酸素極（カソード）側を白金カーボンTEC10V50E（田中貴金属工業（株）製）が塗工されたカーボンクロスで挟み、

膜電極接合体（ＭＥＡ）を作製した。

The membrane electrode assembly thus obtained was incorporated into a fuel cell (manufactured by Toyo Corporation).
この膜電極接合体を燃料電池セル（東陽テクニカ社製）に組み込んで燃料電池セルを作製した。

EP2041824

[0002] The present invention pertains generally to catalysts and more particularly to oxygen reduction catalysts.
【０００２】
  発明の分野
  本発明は一般に触媒に関し、詳しくは酸素還元触媒に関する。

In particular, the present invention relates to catalysts that may be used in oxygen electrodes of fuel cells.
詳しくは、本発明は燃料電池の酸素極に使用される触媒に関する。

////////

[0005] In an alkaline fuel cell, the reaction at the hydrogen electrode occurs between hydrogen and hydroxyl ions (OH- ) present in the electrolyte that form water and release electrons:
【０００５】
  アルカリ燃料電池では、電解液中に存在する水素イオンとヒドロキシルイオン（ＯＨ^－）との以下の反応が水素極において生じ、水および放出電子が形成される。